編號：CPJS01425
篇名：氨改性的介孔二氧化硅的直接合成和CO2吸附（英文）
作者：胡智輝,； 張東輝； 王紀孝,；
關鍵詞：amine-functionalize mesoporous silica,； CO2 adsorption； N2 adsorption,；
機構： Chemical Engineering Research Center,State Key Laboratory of Chemical Engineering,School of Chemical
摘要： Amine-functionalized mesoporous silica was prepared by using lauric acid and N-stearoyl-l-glutamic acid as structure directing agents via the S-N+-I- mechanism and applied to CO2 adsorption at room temperature. With γ-aminopropyltriethoxysilane as co-structure directing agent and due to the direct electrostatic interaction with anionic surfactant, most of the amino groups were uniformly distributed at the inner surface of pores and the per- formance was stable. The amine-functionalized mesoporous silica was characterized by Fourier transform infrared spectrometer, X-ray diffraction, nitrogen physisorption and thermogravimetric analysis. The CO2 adsorption capacity was measured by digital recording balance. At the room temperature and under the atmospheric pressure, the adsorption capacity of LAA-AMS-0.2 for CO2 and N2 is 1.40 mmol·g-1 and 0.03 mmol·g-1, respectively, indicating high separation coefficient of CO2/N2.