超細(xì)氫氧化鈣粉體的原位表面改性研究

編號：FTJS00444

篇名：超細(xì)氫氧化鈣粉體的原位表面改性研究

作者：劉欣萍;

關(guān)鍵詞：氫氧化鈣; 表面活性劑; 原位改性;

機(jī)構(gòu)： 福建師范大學(xué)化學(xué)與材料學(xué)院;

摘要： 在氧化鈣消化成氫氧化鈣的過程中添加表面活性劑對其表面進(jìn)行原位改性,通過測定改性后氫氧化鈣的吸油值,、粘度、吸水率,、沉降體積,、FTIR、SEM的變化等評價其表面改性效果,。結(jié)果表明:改性后氫氧化鈣的吸油值,、粘度、吸水率,、沉降體積均有所下降,表面極性有所減弱,紅外分析說明KH-570偶聯(lián)劑和氫氧化鈣之間存在一定的吸附,。KH-570改性Ca(OH)2比未改性Ca(OH)2分散性好,粒度較小。 Modified calcium hydroxide was synthesized by adding surface activator during slaking of calcium oxide and the oil-absorbed value,viscosity,water-absorption ratio and sedimentation volume of calcium hydroxide were investigated.The results showed that the oil-absorbed value,viscosity,water-absorption ratio and sedimentation volume of calcium hydroxide declined.The adsorption of KH-570 on calcium hydroxide was measured by FTIR,SEM and the dispersion of modified calcium hydroxide was better.