納米碳酸鈣在PVC型材中應(yīng)用研究

編號(hào)：SLHY00051

篇名：納米碳酸鈣在PVC型材中應(yīng)用研究

作者：王道俊;

關(guān)鍵詞：納米碳酸鈣; PVC型材; 增韌增強(qiáng);

機(jī)構(gòu)： 同濟(jì)大學(xué)材料科學(xué)與工程學(xué)院 上海200092安徽省產(chǎn)品質(zhì)量監(jiān)督檢驗(yàn)所;

摘要： 研究納米碳酸鈣(CaCO_3)在PVC/CPE體系中的應(yīng)用,討論了改進(jìn)前后納米CaCO_3對(duì)PVC體系流變行為的影響,并測(cè)試了納米CaCO_3對(duì)型材性能的影響。結(jié)果表明,改進(jìn)后納米CaCO_3 P100流變性接近生產(chǎn)試樣,可用于擠出生產(chǎn);改進(jìn)后的納米CaCO_3顯著提高了型材的性能,可增韌增強(qiáng)PVC復(fù)合體系,。 Use of nanometer calcium carbonate(CaCO_3)in PVC/CPE was studied,effects of nano- CaCO_3 prior and after modification on rheological behaviour of PVC sustemwere discussed and effects of nano-CaCO_3 on performance of the profile were tested.Testing results showed that rheology of the nano-CaCO_3 P100 after modification was almost the same as that of the sample.The nano-CaCO_3 P100 after modification enhanced performance of the profile could be used for extrusion to toughen PVC composite system.K